High Quality Film Faced Plywood 4x8ft 12mm Building Construction
Corrosion Resistance Eucalyptus Melamine Plywood
Product Description Of Melamine Plywood Board:
This film faced plywood is engineered for heavy-duty construction
applications, combining a durable melamine-coated surface with a
robust eucalyptus wood core. Designed in a standard 4x8ft size and
12mm thickness, it offers exceptional dimensional stability and
load-bearing capacity, making it ideal for concrete formwork,
structural frameworks, and industrial flooring systems. The
phenolic film coating provides superior moisture resistance,
ensuring longevity in humid environments and repeated use
scenarios.
Product Features Of Melamine Plywood Board:
1. Triple-layered melamine film surface enhances scratch resistance
and surface smoothness.
2. Cross-laminated eucalyptus core with 11-ply construction for
uniform strength distribution.
3. BS 1088-certified waterproof phenolic resin adhesive bonding.
4. Pre-drilled installation holes along edges for rapid assembly
(optional).
5. UV-treated film layer prevents yellowing under prolonged
sunlight exposure.
Technical Specifications Of Melamine Plywood Board:
- Panel Size: 1220mm x 2440mm (4ft x 8ft).
- Core Material: Grade A Eucalyptus (97% heartwood content).
- Surface Coating: 220g/m² melamine-impregnated paper.
- Glue Type: WBP (Weather & Boil Proof) Phenolic Resin.
- Bending Strength: ≥30MPa (JIS A 5908 standard).
- Thermal Conductivity: 0.12 W/m·K.
- Repeated Usage Cycles: 15-20 times for concrete forming.
- Edge Sealing: Waterproof tape pre-applied on all four sides.
Application Scenarios Of Melamine Plywood Board :
- High-rise building concrete formwork systems.
- Bridge construction shuttering applications.
- Marine infrastructure projects (piers, docks).
- Industrial warehouse flooring substrates.
- Temporary road surfaces for heavy equipment.
- Exhibition stand structural panels.
This construction-grade plywood exceeds ASTM D5456 standards for
structural composite lumber, featuring a unique 3-2-3 ply
configuration that optimizes weight-to-strength ratio. The
eucalyptus core's natural oil content enhances moisture resistance
while the triple-layer film coating provides chemical resistance
against concrete alkalinity (pH up to 13.5). Installation
efficiency is improved through standardized sizing compatibility
with global formwork systems, reducing on-site cutting waste by
approximately 18%.